Lead Zirconate Titanate Dispersion (O5PbTiZr, Purity: 99.9%, Diameter: 100-150nm)

Typical Properties
CAS	12626-81-2
Catalog	ACM12626812-5
Molecular Weight	378.2898 g/mol
Purity	99.9 %
Density	7.7 g/cm3
Appearance	Liquid (Suspension)
Storage	2-8 °C
Composition	O2PbTiZr
Concentration	2 % in Organic Solvent
Diameter	100-150 nm
Precautions for use	According to different application fields, add the appropriate dosage. It is recommended to do a sample test before use.
Shipping	Ventilation, low temperature and dry
Solvent	Organic Solvent
Stability	Long-term placement still remains monodisperse nanoparticles. It can be diluted many times and still maintain monodisperse stability.

Overview

Description

Binary piezoelectric ceramic lead zirconate titanate (PbZrxTi1-xO3 referred to as PZT) is currently the most widely used piezoelectric ferroelectric ceramic material. It has received extensive attention due to its excellent piezoelectric, dielectric and pyroelectric properties. Lead zirconate titanate is a solid solution of PbZrO3 and PbTiO3, with an ABO3 type perovskite structure. PbTiO3 and PbZrO3 are ferroelectric and antiferroelectric The typical representative of , Zr and Ti belong to the same subgroup, PbTiO3 and PbZrO3 have similar spatial lattice forms, but the macroscopic properties of the two are very different, such a big difference has aroused extensive attention, research on titanic acid The solid solution of lead and lead zirconate was found to have better piezoelectric and dielectric properties than other ferroelectrics.

Features

·Uniform particle size
·Good dispersion
·Excellent compatibility
·Chemically stable
·Safety and environmental protection

Application

·Industrial equipment (flow meters, non-destructive testing equipment)
·Automotive (parking sensors, diesel injectors)
·Medical (ultrasound, surgical tools)
·Consumer goods (inkjet printheads, hard drives)